Effect of a fluoridated etchant on the shear bond strength of a composite resin to enamel

Franklin Garcia-Godoy, WILLIAM W. DODGE, MARLA DONOHUE, JULIE A. O'QUINN

Research output: Contribution to journalArticle

1 Citation (Scopus)

Abstract

Summary. The purpose of this study was to evaluate the effect of a fluoridated etching gel on the shear bond strength of a composite resin to enamel. A total of 75 extracted human permanent molars were used. A flat enamel surface was obtained with 600‐grit silicon carbide paper and cleaned with a rubber cup and a water slurry of fine flour of pumice. The teeth were randomly distributed into 5 groups of 15 teeth each and etched as follows: group 1: 37% non‐fluoridated phosphoric acid gel (Coe) for 60 seconds (control); group 2:60% phosphoric acid gel with 0·5% NaF (Orthoprep) for 5 seconds; group 3: Orthoprep for 15 seconds; group 4: Orthoprep for 30 seconds; group 5: Orthoprep for 60 seconds. After etching, rinsing and drying, an unfilled resin (Coe Bond) was thinly applied with a brush and cured for 30 seconds. A nylon ring was placed over the area and filled with a light‐cured composite resin (Occlusin). The teeth were thermocycled (100×), mounted in plastic cups and plaster, and sheared with a knife‐edged blade in an Instron machine running at a crosshead speed of 1 mm/min. The results in MPa were as follows: group 1: 14·49±4·43; group 2: 10·81 ±3·70; group 3: 13·51 ±3·21; group 4: 14·79±3·76; group 5: 15·47 ± 4·07. An analysis of variance showed that the results in groups 1, 4 and 5 were not significantly different but that the bond strengths in groups 2 and 3 were significantly lower. Fracture within the enamel occurred in 8 specimens in group 1, 5 in group 2, 6 in group 3, 8 in group 4, and 13 in group 5. In the fluoridated etchant groups the number of specimens showing enamel fracture increased as the application time of the etchant increased. Le but de cette étude est d'évaluer le résultat de l'utilisation d'un gel fluoré pour etching sur la résistance du collage d'un composite à l'émail. 75 molaires permanentes humaines ont été utilisées. Une surface d'émail plane a été obtenue par un disque de carbone siliconé et nettoyée par une cupulé en caoutchouc et une pâte à polir à base de pierre ponce. Les dents ont été réparties au hasard en groupe de cinq dents chacunes et ont été étchées de la façon suivante: Group N° 1: gel d'acide phosphorique à 37% non fluoré (Coe) pendant 60 secondes (groupe de contrôle); Groupe N° 2: gel d'acide phosphorique à 60% avec 0,5% de fluorure de sodium (Orthoprep) pendant 5 secondes; Groupe N° 3: Orthoprep pendant 15 secondes; Groupe N° 4: Orthoprep pendant 30 secondes; Groupe N° 5: Orthoprep pendant 60 secondes. Après etching, rinçage et séchage, une résine non chargée (Coc Bond) a été appliquée à l'aide d'un pinceau en couche mince et polymérisée pendant 30 secondes. Une bague de nylon a été placée au‐dessus de cette zône et remplie avec un composite (occlusin). Les dents ont été thermocyclées, montées dans un bloc de plastique et du plâtre et coupées en lamelles par une machine Instrom à la vitesse moyenne de 1 millimètre/minute. Les résultats sont les suivants: Groupe N° 1: 14,49±4,43; Groupe N° 2:10,81±3,70; Groupe N° 3: 13,51±3,21; Groupe N° 4: 14,79±3,75; Groupe N° 5: 15,47 ±4.07. L'analyse de variance a montré que les résultats des Groupes N° 1, 4 et 5 n'étaient pas statistiquement différents mais que la résistance du collage dans les Groupes N° 2 et 3 était plus basse de façon significative. Une fracture au niveau de l'émail est apparue dans huit spécimens du Group N° 1, cinq du Groupe N° 2, six du Groupe N° 3, huit du Groupe N° 4 et treize du Groupe N° 5. Dans le groupe avec utilisation du gel fluoré, le nombre de fractures de l'émail a augmenté avec la durée d'application de l'etching. Les résultats sont en faveur de l'utilisation d'un gel fluoré pour etching pendant 30 à 60 secondes. Der Zweck dieser Studie war es zu beurteilen, der Effekt der Anwendung eines fluoridierten Säure‐Gels auf der Haftung des Komposits auf dem Schmelz. 75 extrahierte bleibende Molaren wurden verwendet. Mittels eines Disces wurde eine flache Schmelzfläche geschliffen und diese mit Bimsstein gereinigt. Diese Zähne wurden in 5 Gruppen von 15 Zähnen eingeteilt und wie folgt angeäzt: Gruppe 1: (Kontrolle) mit 37% nicht fluoridierten Gel, 60 sek; Gruppe 2: mit 60% Phosphorsäure welche 0,5 NaF beinhaltet, 5 sek; Gruppe 3: wie Gruppe 2 während 15 sek; Gruppe 4: dito während 30 sek; Gruppe 5: dito während 60 sek. Nach dem Anätzen, Spülen und Trockhen wurde ein ungefülter Kunststoff dünn aufgetragen und während 30 sek polimersiert. Darauf wurde ein Gummiring plaziert und mit Komposit gefüllt und lichtgehärtet. Die Zähne wurden eingesetzt und die Haftung mit einer Instrommaschine geprüft. Die Resultate zeigten, keine Unterschiede in den Gruppen 1, 4 and 5. Die Haftung in den Gruppen 2 und 3 war wesentlich niedriger. In den Gruppen, bei weichen fluoridierter Gel verwendet wurde fand man eins grössere Anzahl von Schmelzfrakturen steigend entsprechend längerer Atzzeiten. El objeto de este estudio fue evaluar el efecto de un gel para grabado ácido conteniendo flúor en la fuerza de unión adhesiva de una resina composite al esmalte. Un total de 75 molares permanentes humanos extraidos fueron utilizados. Una superficie plana de esmalte fue obtenida utilizando papel de sílice de carburo (grado 600) y limpiados con un a copa de goma y piedra pómez. Los dientes fueron distribuídos al azar en 5 grupos de 15 dientes cada uno y grabados con ácido de la siguiente forma: Grupo 1: Gel con 37% ácido fosfórico (Coe) por 60 segundos (control); Grupo 2: Gel con 60% de ácido fosfórico y 0·5% NaF (Orthoprep) por 5 segundos; Grupo 3: Orthoprep por 15 segundos; Grupo 4: Orthoprep por 30 segundos; Grupo 5: Orthoprep por 60 segundos. Despues del grabado ácido, lavado con agua y secado, una delgada capa de una resina de unión (Coe Bond) fue aplicada con un pincel y polimerizada con luz por 30 segundos. Un anillo de nylon fue colocado sobre el area grabada y llenado con una resina composite curada por luz (Occlusin). Los dientes fueron entonces sometidos a ciclos térmicos (100 veces), montados en recipientes plásticos y seccionados con una máquina Instron. Los resultados en MPa fueron los siguientes: Grupo 1: 14·49 ± 4·43; Grupo 2: 10·81 ±3·70; Grupo 3: 13·51 ±3·21; Grupo 4: 14·79±3·76; Grupo 5: 15·47±4·07. El analisis de varianza mostró que los resultados de los grupos 1, 4 y 5 no fueron significativamente estadísticos pero la unión de los grupos 2 y 3 fueron significativamente mas bajos. La fractura del esmalte ocurrió en 8 dientes del Grupo 1, 5 del Grupo 2, 6 del Grupo 3, 8 del Grupo 4 y 13 del Grupo 5. En los grupos utilizando el gel con flúor, el número de especímenes mostrando fractura del esmalte aumentó a medida que el tiempo de aplicación del agente de grabado aumentó. Los resultados dan apoyo al uso del gel con flúor por 30 o 60 segundos para procedimientos adhesivos. 1992 BSPD, IAPD and Blackwell Publishing Ltd

Original languageEnglish (US)
Pages (from-to)25-30
Number of pages6
JournalInternational Journal of Paediatric Dentistry
Volume2
Issue number1
DOIs
StatePublished - Jan 1 1992
Externally publishedYes

Fingerprint

Shear Strength
Composite Resins
Dental Enamel
Gels
Postal Service
Nylons
Tooth
Piedra
Analysis of Variance
Temazepam
Rubber
Flour
Silicon

All Science Journal Classification (ASJC) codes

  • Dentistry(all)

Cite this

Effect of a fluoridated etchant on the shear bond strength of a composite resin to enamel. / Garcia-Godoy, Franklin; DODGE, WILLIAM W.; DONOHUE, MARLA; O'QUINN, JULIE A.

In: International Journal of Paediatric Dentistry, Vol. 2, No. 1, 01.01.1992, p. 25-30.

Research output: Contribution to journalArticle

@article{37605660f4be43e99f4f9e0aceb9524f,
title = "Effect of a fluoridated etchant on the shear bond strength of a composite resin to enamel",
abstract = "Summary. The purpose of this study was to evaluate the effect of a fluoridated etching gel on the shear bond strength of a composite resin to enamel. A total of 75 extracted human permanent molars were used. A flat enamel surface was obtained with 600‐grit silicon carbide paper and cleaned with a rubber cup and a water slurry of fine flour of pumice. The teeth were randomly distributed into 5 groups of 15 teeth each and etched as follows: group 1: 37{\%} non‐fluoridated phosphoric acid gel (Coe) for 60 seconds (control); group 2:60{\%} phosphoric acid gel with 0·5{\%} NaF (Orthoprep) for 5 seconds; group 3: Orthoprep for 15 seconds; group 4: Orthoprep for 30 seconds; group 5: Orthoprep for 60 seconds. After etching, rinsing and drying, an unfilled resin (Coe Bond) was thinly applied with a brush and cured for 30 seconds. A nylon ring was placed over the area and filled with a light‐cured composite resin (Occlusin). The teeth were thermocycled (100×), mounted in plastic cups and plaster, and sheared with a knife‐edged blade in an Instron machine running at a crosshead speed of 1 mm/min. The results in MPa were as follows: group 1: 14·49±4·43; group 2: 10·81 ±3·70; group 3: 13·51 ±3·21; group 4: 14·79±3·76; group 5: 15·47 ± 4·07. An analysis of variance showed that the results in groups 1, 4 and 5 were not significantly different but that the bond strengths in groups 2 and 3 were significantly lower. Fracture within the enamel occurred in 8 specimens in group 1, 5 in group 2, 6 in group 3, 8 in group 4, and 13 in group 5. In the fluoridated etchant groups the number of specimens showing enamel fracture increased as the application time of the etchant increased. Le but de cette {\'e}tude est d'{\'e}valuer le r{\'e}sultat de l'utilisation d'un gel fluor{\'e} pour etching sur la r{\'e}sistance du collage d'un composite {\`a} l'{\'e}mail. 75 molaires permanentes humaines ont {\'e}t{\'e} utilis{\'e}es. Une surface d'{\'e}mail plane a {\'e}t{\'e} obtenue par un disque de carbone silicon{\'e} et nettoy{\'e}e par une cupul{\'e} en caoutchouc et une p{\^a}te {\`a} polir {\`a} base de pierre ponce. Les dents ont {\'e}t{\'e} r{\'e}parties au hasard en groupe de cinq dents chacunes et ont {\'e}t{\'e} {\'e}tch{\'e}es de la fa{\cc}on suivante: Group N° 1: gel d'acide phosphorique {\`a} 37{\%} non fluor{\'e} (Coe) pendant 60 secondes (groupe de contr{\^o}le); Groupe N° 2: gel d'acide phosphorique {\`a} 60{\%} avec 0,5{\%} de fluorure de sodium (Orthoprep) pendant 5 secondes; Groupe N° 3: Orthoprep pendant 15 secondes; Groupe N° 4: Orthoprep pendant 30 secondes; Groupe N° 5: Orthoprep pendant 60 secondes. Apr{\`e}s etching, rin{\cc}age et s{\'e}chage, une r{\'e}sine non charg{\'e}e (Coc Bond) a {\'e}t{\'e} appliqu{\'e}e {\`a} l'aide d'un pinceau en couche mince et polym{\'e}ris{\'e}e pendant 30 secondes. Une bague de nylon a {\'e}t{\'e} plac{\'e}e au‐dessus de cette z{\^o}ne et remplie avec un composite (occlusin). Les dents ont {\'e}t{\'e} thermocycl{\'e}es, mont{\'e}es dans un bloc de plastique et du pl{\^a}tre et coup{\'e}es en lamelles par une machine Instrom {\`a} la vitesse moyenne de 1 millim{\`e}tre/minute. Les r{\'e}sultats sont les suivants: Groupe N° 1: 14,49±4,43; Groupe N° 2:10,81±3,70; Groupe N° 3: 13,51±3,21; Groupe N° 4: 14,79±3,75; Groupe N° 5: 15,47 ±4.07. L'analyse de variance a montr{\'e} que les r{\'e}sultats des Groupes N° 1, 4 et 5 n'{\'e}taient pas statistiquement diff{\'e}rents mais que la r{\'e}sistance du collage dans les Groupes N° 2 et 3 {\'e}tait plus basse de fa{\cc}on significative. Une fracture au niveau de l'{\'e}mail est apparue dans huit sp{\'e}cimens du Group N° 1, cinq du Groupe N° 2, six du Groupe N° 3, huit du Groupe N° 4 et treize du Groupe N° 5. Dans le groupe avec utilisation du gel fluor{\'e}, le nombre de fractures de l'{\'e}mail a augment{\'e} avec la dur{\'e}e d'application de l'etching. Les r{\'e}sultats sont en faveur de l'utilisation d'un gel fluor{\'e} pour etching pendant 30 {\`a} 60 secondes. Der Zweck dieser Studie war es zu beurteilen, der Effekt der Anwendung eines fluoridierten S{\"a}ure‐Gels auf der Haftung des Komposits auf dem Schmelz. 75 extrahierte bleibende Molaren wurden verwendet. Mittels eines Disces wurde eine flache Schmelzfl{\"a}che geschliffen und diese mit Bimsstein gereinigt. Diese Z{\"a}hne wurden in 5 Gruppen von 15 Z{\"a}hnen eingeteilt und wie folgt ange{\"a}zt: Gruppe 1: (Kontrolle) mit 37{\%} nicht fluoridierten Gel, 60 sek; Gruppe 2: mit 60{\%} Phosphors{\"a}ure welche 0,5 NaF beinhaltet, 5 sek; Gruppe 3: wie Gruppe 2 w{\"a}hrend 15 sek; Gruppe 4: dito w{\"a}hrend 30 sek; Gruppe 5: dito w{\"a}hrend 60 sek. Nach dem An{\"a}tzen, Sp{\"u}len und Trockhen wurde ein ungef{\"u}lter Kunststoff d{\"u}nn aufgetragen und w{\"a}hrend 30 sek polimersiert. Darauf wurde ein Gummiring plaziert und mit Komposit gef{\"u}llt und lichtgeh{\"a}rtet. Die Z{\"a}hne wurden eingesetzt und die Haftung mit einer Instrommaschine gepr{\"u}ft. Die Resultate zeigten, keine Unterschiede in den Gruppen 1, 4 and 5. Die Haftung in den Gruppen 2 und 3 war wesentlich niedriger. In den Gruppen, bei weichen fluoridierter Gel verwendet wurde fand man eins gr{\"o}ssere Anzahl von Schmelzfrakturen steigend entsprechend l{\"a}ngerer Atzzeiten. El objeto de este estudio fue evaluar el efecto de un gel para grabado {\'a}cido conteniendo fl{\'u}or en la fuerza de uni{\'o}n adhesiva de una resina composite al esmalte. Un total de 75 molares permanentes humanos extraidos fueron utilizados. Una superficie plana de esmalte fue obtenida utilizando papel de s{\'i}lice de carburo (grado 600) y limpiados con un a copa de goma y piedra p{\'o}mez. Los dientes fueron distribu{\'i}dos al azar en 5 grupos de 15 dientes cada uno y grabados con {\'a}cido de la siguiente forma: Grupo 1: Gel con 37{\%} {\'a}cido fosf{\'o}rico (Coe) por 60 segundos (control); Grupo 2: Gel con 60{\%} de {\'a}cido fosf{\'o}rico y 0·5{\%} NaF (Orthoprep) por 5 segundos; Grupo 3: Orthoprep por 15 segundos; Grupo 4: Orthoprep por 30 segundos; Grupo 5: Orthoprep por 60 segundos. Despues del grabado {\'a}cido, lavado con agua y secado, una delgada capa de una resina de uni{\'o}n (Coe Bond) fue aplicada con un pincel y polimerizada con luz por 30 segundos. Un anillo de nylon fue colocado sobre el area grabada y llenado con una resina composite curada por luz (Occlusin). Los dientes fueron entonces sometidos a ciclos t{\'e}rmicos (100 veces), montados en recipientes pl{\'a}sticos y seccionados con una m{\'a}quina Instron. Los resultados en MPa fueron los siguientes: Grupo 1: 14·49 ± 4·43; Grupo 2: 10·81 ±3·70; Grupo 3: 13·51 ±3·21; Grupo 4: 14·79±3·76; Grupo 5: 15·47±4·07. El analisis de varianza mostr{\'o} que los resultados de los grupos 1, 4 y 5 no fueron significativamente estad{\'i}sticos pero la uni{\'o}n de los grupos 2 y 3 fueron significativamente mas bajos. La fractura del esmalte ocurri{\'o} en 8 dientes del Grupo 1, 5 del Grupo 2, 6 del Grupo 3, 8 del Grupo 4 y 13 del Grupo 5. En los grupos utilizando el gel con fl{\'u}or, el n{\'u}mero de espec{\'i}menes mostrando fractura del esmalte aument{\'o} a medida que el tiempo de aplicaci{\'o}n del agente de grabado aument{\'o}. Los resultados dan apoyo al uso del gel con fl{\'u}or por 30 o 60 segundos para procedimientos adhesivos. 1992 BSPD, IAPD and Blackwell Publishing Ltd",
author = "Franklin Garcia-Godoy and DODGE, {WILLIAM W.} and MARLA DONOHUE and O'QUINN, {JULIE A.}",
year = "1992",
month = "1",
day = "1",
doi = "10.1111/j.1365-263X.1992.tb00004.x",
language = "English (US)",
volume = "2",
pages = "25--30",
journal = "International Journal of Paediatric Dentistry",
issn = "0960-7439",
publisher = "Wiley-Blackwell",
number = "1",

}

TY - JOUR

T1 - Effect of a fluoridated etchant on the shear bond strength of a composite resin to enamel

AU - Garcia-Godoy, Franklin

AU - DODGE, WILLIAM W.

AU - DONOHUE, MARLA

AU - O'QUINN, JULIE A.

PY - 1992/1/1

Y1 - 1992/1/1

N2 - Summary. The purpose of this study was to evaluate the effect of a fluoridated etching gel on the shear bond strength of a composite resin to enamel. A total of 75 extracted human permanent molars were used. A flat enamel surface was obtained with 600‐grit silicon carbide paper and cleaned with a rubber cup and a water slurry of fine flour of pumice. The teeth were randomly distributed into 5 groups of 15 teeth each and etched as follows: group 1: 37% non‐fluoridated phosphoric acid gel (Coe) for 60 seconds (control); group 2:60% phosphoric acid gel with 0·5% NaF (Orthoprep) for 5 seconds; group 3: Orthoprep for 15 seconds; group 4: Orthoprep for 30 seconds; group 5: Orthoprep for 60 seconds. After etching, rinsing and drying, an unfilled resin (Coe Bond) was thinly applied with a brush and cured for 30 seconds. A nylon ring was placed over the area and filled with a light‐cured composite resin (Occlusin). The teeth were thermocycled (100×), mounted in plastic cups and plaster, and sheared with a knife‐edged blade in an Instron machine running at a crosshead speed of 1 mm/min. The results in MPa were as follows: group 1: 14·49±4·43; group 2: 10·81 ±3·70; group 3: 13·51 ±3·21; group 4: 14·79±3·76; group 5: 15·47 ± 4·07. An analysis of variance showed that the results in groups 1, 4 and 5 were not significantly different but that the bond strengths in groups 2 and 3 were significantly lower. Fracture within the enamel occurred in 8 specimens in group 1, 5 in group 2, 6 in group 3, 8 in group 4, and 13 in group 5. In the fluoridated etchant groups the number of specimens showing enamel fracture increased as the application time of the etchant increased. Le but de cette étude est d'évaluer le résultat de l'utilisation d'un gel fluoré pour etching sur la résistance du collage d'un composite à l'émail. 75 molaires permanentes humaines ont été utilisées. Une surface d'émail plane a été obtenue par un disque de carbone siliconé et nettoyée par une cupulé en caoutchouc et une pâte à polir à base de pierre ponce. Les dents ont été réparties au hasard en groupe de cinq dents chacunes et ont été étchées de la façon suivante: Group N° 1: gel d'acide phosphorique à 37% non fluoré (Coe) pendant 60 secondes (groupe de contrôle); Groupe N° 2: gel d'acide phosphorique à 60% avec 0,5% de fluorure de sodium (Orthoprep) pendant 5 secondes; Groupe N° 3: Orthoprep pendant 15 secondes; Groupe N° 4: Orthoprep pendant 30 secondes; Groupe N° 5: Orthoprep pendant 60 secondes. Après etching, rinçage et séchage, une résine non chargée (Coc Bond) a été appliquée à l'aide d'un pinceau en couche mince et polymérisée pendant 30 secondes. Une bague de nylon a été placée au‐dessus de cette zône et remplie avec un composite (occlusin). Les dents ont été thermocyclées, montées dans un bloc de plastique et du plâtre et coupées en lamelles par une machine Instrom à la vitesse moyenne de 1 millimètre/minute. Les résultats sont les suivants: Groupe N° 1: 14,49±4,43; Groupe N° 2:10,81±3,70; Groupe N° 3: 13,51±3,21; Groupe N° 4: 14,79±3,75; Groupe N° 5: 15,47 ±4.07. L'analyse de variance a montré que les résultats des Groupes N° 1, 4 et 5 n'étaient pas statistiquement différents mais que la résistance du collage dans les Groupes N° 2 et 3 était plus basse de façon significative. Une fracture au niveau de l'émail est apparue dans huit spécimens du Group N° 1, cinq du Groupe N° 2, six du Groupe N° 3, huit du Groupe N° 4 et treize du Groupe N° 5. Dans le groupe avec utilisation du gel fluoré, le nombre de fractures de l'émail a augmenté avec la durée d'application de l'etching. Les résultats sont en faveur de l'utilisation d'un gel fluoré pour etching pendant 30 à 60 secondes. Der Zweck dieser Studie war es zu beurteilen, der Effekt der Anwendung eines fluoridierten Säure‐Gels auf der Haftung des Komposits auf dem Schmelz. 75 extrahierte bleibende Molaren wurden verwendet. Mittels eines Disces wurde eine flache Schmelzfläche geschliffen und diese mit Bimsstein gereinigt. Diese Zähne wurden in 5 Gruppen von 15 Zähnen eingeteilt und wie folgt angeäzt: Gruppe 1: (Kontrolle) mit 37% nicht fluoridierten Gel, 60 sek; Gruppe 2: mit 60% Phosphorsäure welche 0,5 NaF beinhaltet, 5 sek; Gruppe 3: wie Gruppe 2 während 15 sek; Gruppe 4: dito während 30 sek; Gruppe 5: dito während 60 sek. Nach dem Anätzen, Spülen und Trockhen wurde ein ungefülter Kunststoff dünn aufgetragen und während 30 sek polimersiert. Darauf wurde ein Gummiring plaziert und mit Komposit gefüllt und lichtgehärtet. Die Zähne wurden eingesetzt und die Haftung mit einer Instrommaschine geprüft. Die Resultate zeigten, keine Unterschiede in den Gruppen 1, 4 and 5. Die Haftung in den Gruppen 2 und 3 war wesentlich niedriger. In den Gruppen, bei weichen fluoridierter Gel verwendet wurde fand man eins grössere Anzahl von Schmelzfrakturen steigend entsprechend längerer Atzzeiten. El objeto de este estudio fue evaluar el efecto de un gel para grabado ácido conteniendo flúor en la fuerza de unión adhesiva de una resina composite al esmalte. Un total de 75 molares permanentes humanos extraidos fueron utilizados. Una superficie plana de esmalte fue obtenida utilizando papel de sílice de carburo (grado 600) y limpiados con un a copa de goma y piedra pómez. Los dientes fueron distribuídos al azar en 5 grupos de 15 dientes cada uno y grabados con ácido de la siguiente forma: Grupo 1: Gel con 37% ácido fosfórico (Coe) por 60 segundos (control); Grupo 2: Gel con 60% de ácido fosfórico y 0·5% NaF (Orthoprep) por 5 segundos; Grupo 3: Orthoprep por 15 segundos; Grupo 4: Orthoprep por 30 segundos; Grupo 5: Orthoprep por 60 segundos. Despues del grabado ácido, lavado con agua y secado, una delgada capa de una resina de unión (Coe Bond) fue aplicada con un pincel y polimerizada con luz por 30 segundos. Un anillo de nylon fue colocado sobre el area grabada y llenado con una resina composite curada por luz (Occlusin). Los dientes fueron entonces sometidos a ciclos térmicos (100 veces), montados en recipientes plásticos y seccionados con una máquina Instron. Los resultados en MPa fueron los siguientes: Grupo 1: 14·49 ± 4·43; Grupo 2: 10·81 ±3·70; Grupo 3: 13·51 ±3·21; Grupo 4: 14·79±3·76; Grupo 5: 15·47±4·07. El analisis de varianza mostró que los resultados de los grupos 1, 4 y 5 no fueron significativamente estadísticos pero la unión de los grupos 2 y 3 fueron significativamente mas bajos. La fractura del esmalte ocurrió en 8 dientes del Grupo 1, 5 del Grupo 2, 6 del Grupo 3, 8 del Grupo 4 y 13 del Grupo 5. En los grupos utilizando el gel con flúor, el número de especímenes mostrando fractura del esmalte aumentó a medida que el tiempo de aplicación del agente de grabado aumentó. Los resultados dan apoyo al uso del gel con flúor por 30 o 60 segundos para procedimientos adhesivos. 1992 BSPD, IAPD and Blackwell Publishing Ltd

AB - Summary. The purpose of this study was to evaluate the effect of a fluoridated etching gel on the shear bond strength of a composite resin to enamel. A total of 75 extracted human permanent molars were used. A flat enamel surface was obtained with 600‐grit silicon carbide paper and cleaned with a rubber cup and a water slurry of fine flour of pumice. The teeth were randomly distributed into 5 groups of 15 teeth each and etched as follows: group 1: 37% non‐fluoridated phosphoric acid gel (Coe) for 60 seconds (control); group 2:60% phosphoric acid gel with 0·5% NaF (Orthoprep) for 5 seconds; group 3: Orthoprep for 15 seconds; group 4: Orthoprep for 30 seconds; group 5: Orthoprep for 60 seconds. After etching, rinsing and drying, an unfilled resin (Coe Bond) was thinly applied with a brush and cured for 30 seconds. A nylon ring was placed over the area and filled with a light‐cured composite resin (Occlusin). The teeth were thermocycled (100×), mounted in plastic cups and plaster, and sheared with a knife‐edged blade in an Instron machine running at a crosshead speed of 1 mm/min. The results in MPa were as follows: group 1: 14·49±4·43; group 2: 10·81 ±3·70; group 3: 13·51 ±3·21; group 4: 14·79±3·76; group 5: 15·47 ± 4·07. An analysis of variance showed that the results in groups 1, 4 and 5 were not significantly different but that the bond strengths in groups 2 and 3 were significantly lower. Fracture within the enamel occurred in 8 specimens in group 1, 5 in group 2, 6 in group 3, 8 in group 4, and 13 in group 5. In the fluoridated etchant groups the number of specimens showing enamel fracture increased as the application time of the etchant increased. Le but de cette étude est d'évaluer le résultat de l'utilisation d'un gel fluoré pour etching sur la résistance du collage d'un composite à l'émail. 75 molaires permanentes humaines ont été utilisées. Une surface d'émail plane a été obtenue par un disque de carbone siliconé et nettoyée par une cupulé en caoutchouc et une pâte à polir à base de pierre ponce. Les dents ont été réparties au hasard en groupe de cinq dents chacunes et ont été étchées de la façon suivante: Group N° 1: gel d'acide phosphorique à 37% non fluoré (Coe) pendant 60 secondes (groupe de contrôle); Groupe N° 2: gel d'acide phosphorique à 60% avec 0,5% de fluorure de sodium (Orthoprep) pendant 5 secondes; Groupe N° 3: Orthoprep pendant 15 secondes; Groupe N° 4: Orthoprep pendant 30 secondes; Groupe N° 5: Orthoprep pendant 60 secondes. Après etching, rinçage et séchage, une résine non chargée (Coc Bond) a été appliquée à l'aide d'un pinceau en couche mince et polymérisée pendant 30 secondes. Une bague de nylon a été placée au‐dessus de cette zône et remplie avec un composite (occlusin). Les dents ont été thermocyclées, montées dans un bloc de plastique et du plâtre et coupées en lamelles par une machine Instrom à la vitesse moyenne de 1 millimètre/minute. Les résultats sont les suivants: Groupe N° 1: 14,49±4,43; Groupe N° 2:10,81±3,70; Groupe N° 3: 13,51±3,21; Groupe N° 4: 14,79±3,75; Groupe N° 5: 15,47 ±4.07. L'analyse de variance a montré que les résultats des Groupes N° 1, 4 et 5 n'étaient pas statistiquement différents mais que la résistance du collage dans les Groupes N° 2 et 3 était plus basse de façon significative. Une fracture au niveau de l'émail est apparue dans huit spécimens du Group N° 1, cinq du Groupe N° 2, six du Groupe N° 3, huit du Groupe N° 4 et treize du Groupe N° 5. Dans le groupe avec utilisation du gel fluoré, le nombre de fractures de l'émail a augmenté avec la durée d'application de l'etching. Les résultats sont en faveur de l'utilisation d'un gel fluoré pour etching pendant 30 à 60 secondes. Der Zweck dieser Studie war es zu beurteilen, der Effekt der Anwendung eines fluoridierten Säure‐Gels auf der Haftung des Komposits auf dem Schmelz. 75 extrahierte bleibende Molaren wurden verwendet. Mittels eines Disces wurde eine flache Schmelzfläche geschliffen und diese mit Bimsstein gereinigt. Diese Zähne wurden in 5 Gruppen von 15 Zähnen eingeteilt und wie folgt angeäzt: Gruppe 1: (Kontrolle) mit 37% nicht fluoridierten Gel, 60 sek; Gruppe 2: mit 60% Phosphorsäure welche 0,5 NaF beinhaltet, 5 sek; Gruppe 3: wie Gruppe 2 während 15 sek; Gruppe 4: dito während 30 sek; Gruppe 5: dito während 60 sek. Nach dem Anätzen, Spülen und Trockhen wurde ein ungefülter Kunststoff dünn aufgetragen und während 30 sek polimersiert. Darauf wurde ein Gummiring plaziert und mit Komposit gefüllt und lichtgehärtet. Die Zähne wurden eingesetzt und die Haftung mit einer Instrommaschine geprüft. Die Resultate zeigten, keine Unterschiede in den Gruppen 1, 4 and 5. Die Haftung in den Gruppen 2 und 3 war wesentlich niedriger. In den Gruppen, bei weichen fluoridierter Gel verwendet wurde fand man eins grössere Anzahl von Schmelzfrakturen steigend entsprechend längerer Atzzeiten. El objeto de este estudio fue evaluar el efecto de un gel para grabado ácido conteniendo flúor en la fuerza de unión adhesiva de una resina composite al esmalte. Un total de 75 molares permanentes humanos extraidos fueron utilizados. Una superficie plana de esmalte fue obtenida utilizando papel de sílice de carburo (grado 600) y limpiados con un a copa de goma y piedra pómez. Los dientes fueron distribuídos al azar en 5 grupos de 15 dientes cada uno y grabados con ácido de la siguiente forma: Grupo 1: Gel con 37% ácido fosfórico (Coe) por 60 segundos (control); Grupo 2: Gel con 60% de ácido fosfórico y 0·5% NaF (Orthoprep) por 5 segundos; Grupo 3: Orthoprep por 15 segundos; Grupo 4: Orthoprep por 30 segundos; Grupo 5: Orthoprep por 60 segundos. Despues del grabado ácido, lavado con agua y secado, una delgada capa de una resina de unión (Coe Bond) fue aplicada con un pincel y polimerizada con luz por 30 segundos. Un anillo de nylon fue colocado sobre el area grabada y llenado con una resina composite curada por luz (Occlusin). Los dientes fueron entonces sometidos a ciclos térmicos (100 veces), montados en recipientes plásticos y seccionados con una máquina Instron. Los resultados en MPa fueron los siguientes: Grupo 1: 14·49 ± 4·43; Grupo 2: 10·81 ±3·70; Grupo 3: 13·51 ±3·21; Grupo 4: 14·79±3·76; Grupo 5: 15·47±4·07. El analisis de varianza mostró que los resultados de los grupos 1, 4 y 5 no fueron significativamente estadísticos pero la unión de los grupos 2 y 3 fueron significativamente mas bajos. La fractura del esmalte ocurrió en 8 dientes del Grupo 1, 5 del Grupo 2, 6 del Grupo 3, 8 del Grupo 4 y 13 del Grupo 5. En los grupos utilizando el gel con flúor, el número de especímenes mostrando fractura del esmalte aumentó a medida que el tiempo de aplicación del agente de grabado aumentó. Los resultados dan apoyo al uso del gel con flúor por 30 o 60 segundos para procedimientos adhesivos. 1992 BSPD, IAPD and Blackwell Publishing Ltd

UR - http://www.scopus.com/inward/record.url?scp=0026843111&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=0026843111&partnerID=8YFLogxK

U2 - 10.1111/j.1365-263X.1992.tb00004.x

DO - 10.1111/j.1365-263X.1992.tb00004.x

M3 - Article

C2 - 1525128

AN - SCOPUS:0026843111

VL - 2

SP - 25

EP - 30

JO - International Journal of Paediatric Dentistry

JF - International Journal of Paediatric Dentistry

SN - 0960-7439

IS - 1

ER -