Effects of various mixing techniques on physical properties of White Mineral Trioxide Aggregate

Mohammad Ali Saghiri, Franklin Garcia-Godoy, James L. Gutmann, Mehrdad Lotfi, Armen Asatourian

Research output: Contribution to journalArticle

4 Citations (Scopus)

Abstract

Introduction: The aim of this study was to evaluate the effects of three different mixing techniques on surface microhardness, initial setting time, and phase formation of white mineral trioxide aggregate. Methods: Twenty-one cylindrical glass tubes were selected and divided into three groups of seven in each (n = 7). White mineral trioxide aggregate (WMTA) in groups A, B, and C were mixed by conventional, trituration, and ultrasonic techniques, respectively. Cements were mixed and packed into the glass tubes and incubated at 37°C for 3 days. After incubation, samples were subjected to microhardness evaluation, and four specimens from each group were prepared and observed under a scanning electron microscopy and X-ray diffraction. For setting time assessment, WMTA was mixed in three parts again, and Gilmore needle test was performed until the initial setting time of cement. Data were analyzed by one-way anova and post hoc Tukey's test. Results: Samples mixed by trituration technique significantly showed the highest microhardness (P < 0.001) and the lowest setting time, while the ultrasonically mixed specimens significantly revealed the highest setting time in comparison with other groups (P < 0.001). Samples mixed by trituration technique showed the highest uniformity in the bulk and highest amount of hydrated calcium silicate (CS) phases, while the lowest value was observed in ultrasonically mixed cements, which also showed the highest amount of anhydrated CS phases. Conclusion: Trituration and conventional techniques were more suitable mixing methods for mineral trioxide aggregate in comparison with ultrasonic technique. Trituration resulted in better hydration and crystallization, which prevents clustering of powder and reduces voids and setting time of mixed cement.

Original languageEnglish (US)
Pages (from-to)240-245
Number of pages6
JournalDental Traumatology
Volume30
Issue number3
DOIs
StatePublished - Jan 1 2014

Fingerprint

Ultrasonics
Glass
Crystallization
X-Ray Diffraction
Electron Scanning Microscopy
Powders
Needles
Cluster Analysis
mineral trioxide aggregate
calcium silicate

All Science Journal Classification (ASJC) codes

  • Oral Surgery

Cite this

Effects of various mixing techniques on physical properties of White Mineral Trioxide Aggregate. / Saghiri, Mohammad Ali; Garcia-Godoy, Franklin; Gutmann, James L.; Lotfi, Mehrdad; Asatourian, Armen.

In: Dental Traumatology, Vol. 30, No. 3, 01.01.2014, p. 240-245.

Research output: Contribution to journalArticle

Saghiri, Mohammad Ali ; Garcia-Godoy, Franklin ; Gutmann, James L. ; Lotfi, Mehrdad ; Asatourian, Armen. / Effects of various mixing techniques on physical properties of White Mineral Trioxide Aggregate. In: Dental Traumatology. 2014 ; Vol. 30, No. 3. pp. 240-245.
@article{8e9b9bf69b6c46c4b6102877e1293454,
title = "Effects of various mixing techniques on physical properties of White Mineral Trioxide Aggregate",
abstract = "Introduction: The aim of this study was to evaluate the effects of three different mixing techniques on surface microhardness, initial setting time, and phase formation of white mineral trioxide aggregate. Methods: Twenty-one cylindrical glass tubes were selected and divided into three groups of seven in each (n = 7). White mineral trioxide aggregate (WMTA) in groups A, B, and C were mixed by conventional, trituration, and ultrasonic techniques, respectively. Cements were mixed and packed into the glass tubes and incubated at 37°C for 3 days. After incubation, samples were subjected to microhardness evaluation, and four specimens from each group were prepared and observed under a scanning electron microscopy and X-ray diffraction. For setting time assessment, WMTA was mixed in three parts again, and Gilmore needle test was performed until the initial setting time of cement. Data were analyzed by one-way anova and post hoc Tukey's test. Results: Samples mixed by trituration technique significantly showed the highest microhardness (P < 0.001) and the lowest setting time, while the ultrasonically mixed specimens significantly revealed the highest setting time in comparison with other groups (P < 0.001). Samples mixed by trituration technique showed the highest uniformity in the bulk and highest amount of hydrated calcium silicate (CS) phases, while the lowest value was observed in ultrasonically mixed cements, which also showed the highest amount of anhydrated CS phases. Conclusion: Trituration and conventional techniques were more suitable mixing methods for mineral trioxide aggregate in comparison with ultrasonic technique. Trituration resulted in better hydration and crystallization, which prevents clustering of powder and reduces voids and setting time of mixed cement.",
author = "Saghiri, {Mohammad Ali} and Franklin Garcia-Godoy and Gutmann, {James L.} and Mehrdad Lotfi and Armen Asatourian",
year = "2014",
month = "1",
day = "1",
doi = "10.1111/edt.12067",
language = "English (US)",
volume = "30",
pages = "240--245",
journal = "Dental Traumatology",
issn = "1600-4469",
publisher = "Blackwell Munksgaard",
number = "3",

}

TY - JOUR

T1 - Effects of various mixing techniques on physical properties of White Mineral Trioxide Aggregate

AU - Saghiri, Mohammad Ali

AU - Garcia-Godoy, Franklin

AU - Gutmann, James L.

AU - Lotfi, Mehrdad

AU - Asatourian, Armen

PY - 2014/1/1

Y1 - 2014/1/1

N2 - Introduction: The aim of this study was to evaluate the effects of three different mixing techniques on surface microhardness, initial setting time, and phase formation of white mineral trioxide aggregate. Methods: Twenty-one cylindrical glass tubes were selected and divided into three groups of seven in each (n = 7). White mineral trioxide aggregate (WMTA) in groups A, B, and C were mixed by conventional, trituration, and ultrasonic techniques, respectively. Cements were mixed and packed into the glass tubes and incubated at 37°C for 3 days. After incubation, samples were subjected to microhardness evaluation, and four specimens from each group were prepared and observed under a scanning electron microscopy and X-ray diffraction. For setting time assessment, WMTA was mixed in three parts again, and Gilmore needle test was performed until the initial setting time of cement. Data were analyzed by one-way anova and post hoc Tukey's test. Results: Samples mixed by trituration technique significantly showed the highest microhardness (P < 0.001) and the lowest setting time, while the ultrasonically mixed specimens significantly revealed the highest setting time in comparison with other groups (P < 0.001). Samples mixed by trituration technique showed the highest uniformity in the bulk and highest amount of hydrated calcium silicate (CS) phases, while the lowest value was observed in ultrasonically mixed cements, which also showed the highest amount of anhydrated CS phases. Conclusion: Trituration and conventional techniques were more suitable mixing methods for mineral trioxide aggregate in comparison with ultrasonic technique. Trituration resulted in better hydration and crystallization, which prevents clustering of powder and reduces voids and setting time of mixed cement.

AB - Introduction: The aim of this study was to evaluate the effects of three different mixing techniques on surface microhardness, initial setting time, and phase formation of white mineral trioxide aggregate. Methods: Twenty-one cylindrical glass tubes were selected and divided into three groups of seven in each (n = 7). White mineral trioxide aggregate (WMTA) in groups A, B, and C were mixed by conventional, trituration, and ultrasonic techniques, respectively. Cements were mixed and packed into the glass tubes and incubated at 37°C for 3 days. After incubation, samples were subjected to microhardness evaluation, and four specimens from each group were prepared and observed under a scanning electron microscopy and X-ray diffraction. For setting time assessment, WMTA was mixed in three parts again, and Gilmore needle test was performed until the initial setting time of cement. Data were analyzed by one-way anova and post hoc Tukey's test. Results: Samples mixed by trituration technique significantly showed the highest microhardness (P < 0.001) and the lowest setting time, while the ultrasonically mixed specimens significantly revealed the highest setting time in comparison with other groups (P < 0.001). Samples mixed by trituration technique showed the highest uniformity in the bulk and highest amount of hydrated calcium silicate (CS) phases, while the lowest value was observed in ultrasonically mixed cements, which also showed the highest amount of anhydrated CS phases. Conclusion: Trituration and conventional techniques were more suitable mixing methods for mineral trioxide aggregate in comparison with ultrasonic technique. Trituration resulted in better hydration and crystallization, which prevents clustering of powder and reduces voids and setting time of mixed cement.

UR - http://www.scopus.com/inward/record.url?scp=84899945129&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=84899945129&partnerID=8YFLogxK

U2 - 10.1111/edt.12067

DO - 10.1111/edt.12067

M3 - Article

VL - 30

SP - 240

EP - 245

JO - Dental Traumatology

JF - Dental Traumatology

SN - 1600-4469

IS - 3

ER -