The effect of etching time with Gluma 2000 conditioning solution on shear bond strength of a composite resin and on micromorphology of the enamel

S. MALFERRARI, W. J. FINGER, Franklin Garcia-Godoy

Research output: Contribution to journalArticle

4 Citations (Scopus)

Abstract

Summary. The purpose of this study was to assess the effect of etching time with Gluma 2000 conditioning agent on, first, the shear bond strength of composite resin to tooth enamel and, secondly, the micromorphology of the enamel. In the first part of the study flat enamel surfaces were prepared with 600‐grit silicon carbide paper on 40 primary and 40 permanent teeth. Ten specimens of each group were etched for 15, 30, 60 or 120 seconds before applying bonding resin and restorative composite resin. After 24 hours' storage in water, the shear bond strength of each specimen was tested. Analysis of variance indicated a significant difference between the eight groups. However, the Student‐Newman‐Keuls test indicated that the only differences that were significant were the greater bond strengths of the 15‐second primary tooth specimens compared with the 15‐ and 30‐second permanent tooth specimens. In most cases the debonded specimens showed cohesive failure in resin close to the coupling interface. In the second part of the study the morphology of the enamel etching patterns in 96 other teeth was studied by scanning electron microscopy. The patterns were similar in primary and permanent teeth, and the longer the etching time the more pronounced was the pattern. The patterns produced in ground enamel were more uniform and predictable than those in pumiced enamel. Examination of bonded resin surfaces after dissolution of the teeth showed complete reproduction of the etched enamel surfaces, indicating excellent flow of the resin into the etched enamel. Le propos de cette étude est d'évaluer le résultat de la durée d'application d'acide, par l'agent de conditionnement Gluma 2000, sur premièrement la force de résistance du lien à l'émail dentaire et, deuxièment, la micromorphologie de l'émail. Dans la première partie de l'étude, des surfaces d'émail planes de 40 dents temporaires et 40 dents permanentes ont été préparées avec un carbure siliconé de 600 grains. Dix spécimens de chaque groupe ont été mordancés à l'acide pendant 15, 30, 60 ou 120 secondes avant application de l'agent de liaison et obturation avec une résine composite. Après immersion dans l'eau pendant vingt‐quatre heures, la résistance de la liaison de l'obturation à chaque spécimen a été testée. l'analyse de variance a montré des différences significatives entre les huit groupes. Mais, le test Student‐Newman‐Keuls a montré que les seules différences significatives étaient la résistance plus importante de la liaison aux 15 molaires temporaires mordancées à l'acide 15 secondes, comparée à celles des dents permanentes traitées 15 et 30 secondes. Dans la majorité des cas, les obturations descellées montraient un défaut de cohésion au niveau de l'interface. Dans la seconde partie de l'étude, la morphologie de l'émail, mordancé à l'acide, de 96 autres dents, a été étudiée au microscope électronique à balayage. Les résultats étaient similaires pour les dents temporaires et permanentes et plus marqués, quand le temps d'application était plus long. Les résultats étaient plus uniformes et prévisibles dans l'émail meulé que dans l'émail poli. l'examen des surfaces de liaison à la résine, après dissolution de la dent, montrait une reproduction des surfaces d'émail mordancé à l'acide; la résine avait donc obturé de façon compléte les microrétentions. Ziel der vorliegenden Untersuchung war die Beurteilung der Wirksamkeit der Gluma 2000 Ätzlösung auf Schmelz von Milchzähnen (DI) und von bleibenden Zähnen (DP). Im ersten Teil der Studie wurden von 40 Milchzähnen (DI) und von 40 bleibenden Zähnen (DP) Schmelzoberflächen mit Sic‐Papier der Körnung 600 präpariert. Zehn Proben jeder Gruppe wurden für 15, 30, 60 oder 120 Sekunden vor Applikation des Haftmittels und Restaurirungskunststoffes geätzt. Nach 24 stündiger lagerung in Wasser wurde vonjeder Probe die Scherbindungsfestigkeit bestimmt. Die Varianz‐analyse zeigte signifkante Unterschiede zwischen acht Gruppen (p = 0.003). Nach dem Student‐Newman‐Keuls Test erwiesen sich nur die Vergleiche DI15 vs DI15 und DI15 vs DP30 als signifikant unterschiedlich. Im zweiten Teil der Studie wurde die Morphologie der Schmelzätzmuster an 96 weiteren Zähnen im Rasterelektronermikroskop untersucht. Je länger die Ätzdauer, umso ausgeprägter war das Ätzmuster. Die auf präpariertem Schmelz erzeugten Äztmuster waren gleichmässiger und vorhersehbarer als die auf nur mit Bimsstein‐behandeltem Schmelz. Der geätzte Schmelz wurde vom adhäsiven Resin vollständig benetzt. Nach Auflösung der Zähne kannte man die vollständigewiedergabe der geäzten Schmelzflächen sehen, was auf den ausergewöhnlichen guten Flow des Kunststoffes in den angeäzten Schmelz hinweist. El Propósito de este trabajo fue evaluar la eficacia de la solución acondicionadora de oxalato de aluminio del agente de unión Gluma 2000 en el esmalte de dientes temporales (DI) y permanentes (DP). Para evaluar la fuerza de unión (SBS) 24 horas despues de almacenar los especímenes en agua, en 40 DI y DP se produjo una superficie plana con papel de SiC grado 600. Diez especímenes de cada grupo fueron grabados por 15, 30, 60 y 120 segundos antes de aplicar el agente de unión y la resina restauradora Pekafill. El análisis de varianza mostró que hubo diferencia significativa (P = 0.0003) entre los 8 grupos. La prueba de Student‐Newman‐Keuls identificó las comparaciones DI15 vs DP15 y DI15 vs DP 30 como las únicas estadísticamente diferentes. La morfología de los patrones de grabado ácido del esmalte evaluados con el microscopio electrónico de barrido mostró que a mayor tempo de grabado, más profundo era el efecto en el esmalte. Los patrones del grabado obtenidos en esmalte tratado con el papel de SiC fueron más uniformes que los obtenidos en el esmalte tratado solo con piedra pómez. El esmalte acondicionado fue perfectamente penetrado con la resina de unión. En la mayoría de los casos, los especímenes mostraron falla cohesiva de la resina muy proxima a la interface con el esmalte. 1994 BSPD, IAPD and Blackwell Publishing Ltd

Original languageEnglish (US)
Pages (from-to)217-224
Number of pages8
JournalInternational Journal of Paediatric Dentistry
Volume4
Issue number4
DOIs
StatePublished - Jan 1 1994
Externally publishedYes

Fingerprint

Shear Strength
Composite Resins
Dental Enamel
Postal Service
Tooth
Deciduous Tooth
Reproduction
Piedra
Analysis of Variance
Temazepam
Gluma 2000
Immersion
Silicon
Electron Scanning Microscopy
Water

All Science Journal Classification (ASJC) codes

  • Dentistry(all)

Cite this

@article{41ffea64fc8649cbb73439feee588b26,
title = "The effect of etching time with Gluma 2000 conditioning solution on shear bond strength of a composite resin and on micromorphology of the enamel",
abstract = "Summary. The purpose of this study was to assess the effect of etching time with Gluma 2000 conditioning agent on, first, the shear bond strength of composite resin to tooth enamel and, secondly, the micromorphology of the enamel. In the first part of the study flat enamel surfaces were prepared with 600‐grit silicon carbide paper on 40 primary and 40 permanent teeth. Ten specimens of each group were etched for 15, 30, 60 or 120 seconds before applying bonding resin and restorative composite resin. After 24 hours' storage in water, the shear bond strength of each specimen was tested. Analysis of variance indicated a significant difference between the eight groups. However, the Student‐Newman‐Keuls test indicated that the only differences that were significant were the greater bond strengths of the 15‐second primary tooth specimens compared with the 15‐ and 30‐second permanent tooth specimens. In most cases the debonded specimens showed cohesive failure in resin close to the coupling interface. In the second part of the study the morphology of the enamel etching patterns in 96 other teeth was studied by scanning electron microscopy. The patterns were similar in primary and permanent teeth, and the longer the etching time the more pronounced was the pattern. The patterns produced in ground enamel were more uniform and predictable than those in pumiced enamel. Examination of bonded resin surfaces after dissolution of the teeth showed complete reproduction of the etched enamel surfaces, indicating excellent flow of the resin into the etched enamel. Le propos de cette {\'e}tude est d'{\'e}valuer le r{\'e}sultat de la dur{\'e}e d'application d'acide, par l'agent de conditionnement Gluma 2000, sur premi{\`e}rement la force de r{\'e}sistance du lien {\`a} l'{\'e}mail dentaire et, deuxi{\`e}ment, la micromorphologie de l'{\'e}mail. Dans la premi{\`e}re partie de l'{\'e}tude, des surfaces d'{\'e}mail planes de 40 dents temporaires et 40 dents permanentes ont {\'e}t{\'e} pr{\'e}par{\'e}es avec un carbure silicon{\'e} de 600 grains. Dix sp{\'e}cimens de chaque groupe ont {\'e}t{\'e} mordanc{\'e}s {\`a} l'acide pendant 15, 30, 60 ou 120 secondes avant application de l'agent de liaison et obturation avec une r{\'e}sine composite. Apr{\`e}s immersion dans l'eau pendant vingt‐quatre heures, la r{\'e}sistance de la liaison de l'obturation {\`a} chaque sp{\'e}cimen a {\'e}t{\'e} test{\'e}e. l'analyse de variance a montr{\'e} des diff{\'e}rences significatives entre les huit groupes. Mais, le test Student‐Newman‐Keuls a montr{\'e} que les seules diff{\'e}rences significatives {\'e}taient la r{\'e}sistance plus importante de la liaison aux 15 molaires temporaires mordanc{\'e}es {\`a} l'acide 15 secondes, compar{\'e}e {\`a} celles des dents permanentes trait{\'e}es 15 et 30 secondes. Dans la majorit{\'e} des cas, les obturations descell{\'e}es montraient un d{\'e}faut de coh{\'e}sion au niveau de l'interface. Dans la seconde partie de l'{\'e}tude, la morphologie de l'{\'e}mail, mordanc{\'e} {\`a} l'acide, de 96 autres dents, a {\'e}t{\'e} {\'e}tudi{\'e}e au microscope {\'e}lectronique {\`a} balayage. Les r{\'e}sultats {\'e}taient similaires pour les dents temporaires et permanentes et plus marqu{\'e}s, quand le temps d'application {\'e}tait plus long. Les r{\'e}sultats {\'e}taient plus uniformes et pr{\'e}visibles dans l'{\'e}mail meul{\'e} que dans l'{\'e}mail poli. l'examen des surfaces de liaison {\`a} la r{\'e}sine, apr{\`e}s dissolution de la dent, montrait une reproduction des surfaces d'{\'e}mail mordanc{\'e} {\`a} l'acide; la r{\'e}sine avait donc obtur{\'e} de fa{\cc}on compl{\'e}te les micror{\'e}tentions. Ziel der vorliegenden Untersuchung war die Beurteilung der Wirksamkeit der Gluma 2000 {\"A}tzl{\"o}sung auf Schmelz von Milchz{\"a}hnen (DI) und von bleibenden Z{\"a}hnen (DP). Im ersten Teil der Studie wurden von 40 Milchz{\"a}hnen (DI) und von 40 bleibenden Z{\"a}hnen (DP) Schmelzoberfl{\"a}chen mit Sic‐Papier der K{\"o}rnung 600 pr{\"a}pariert. Zehn Proben jeder Gruppe wurden f{\"u}r 15, 30, 60 oder 120 Sekunden vor Applikation des Haftmittels und Restaurirungskunststoffes ge{\"a}tzt. Nach 24 st{\"u}ndiger lagerung in Wasser wurde vonjeder Probe die Scherbindungsfestigkeit bestimmt. Die Varianz‐analyse zeigte signifkante Unterschiede zwischen acht Gruppen (p = 0.003). Nach dem Student‐Newman‐Keuls Test erwiesen sich nur die Vergleiche DI15 vs DI15 und DI15 vs DP30 als signifikant unterschiedlich. Im zweiten Teil der Studie wurde die Morphologie der Schmelz{\"a}tzmuster an 96 weiteren Z{\"a}hnen im Rasterelektronermikroskop untersucht. Je l{\"a}nger die {\"A}tzdauer, umso ausgepr{\"a}gter war das {\"A}tzmuster. Die auf pr{\"a}pariertem Schmelz erzeugten {\"A}ztmuster waren gleichm{\"a}ssiger und vorhersehbarer als die auf nur mit Bimsstein‐behandeltem Schmelz. Der ge{\"a}tzte Schmelz wurde vom adh{\"a}siven Resin vollst{\"a}ndig benetzt. Nach Aufl{\"o}sung der Z{\"a}hne kannte man die vollst{\"a}ndigewiedergabe der ge{\"a}zten Schmelzfl{\"a}chen sehen, was auf den ausergew{\"o}hnlichen guten Flow des Kunststoffes in den ange{\"a}zten Schmelz hinweist. El Prop{\'o}sito de este trabajo fue evaluar la eficacia de la soluci{\'o}n acondicionadora de oxalato de aluminio del agente de uni{\'o}n Gluma 2000 en el esmalte de dientes temporales (DI) y permanentes (DP). Para evaluar la fuerza de uni{\'o}n (SBS) 24 horas despues de almacenar los espec{\'i}menes en agua, en 40 DI y DP se produjo una superficie plana con papel de SiC grado 600. Diez espec{\'i}menes de cada grupo fueron grabados por 15, 30, 60 y 120 segundos antes de aplicar el agente de uni{\'o}n y la resina restauradora Pekafill. El an{\'a}lisis de varianza mostr{\'o} que hubo diferencia significativa (P = 0.0003) entre los 8 grupos. La prueba de Student‐Newman‐Keuls identific{\'o} las comparaciones DI15 vs DP15 y DI15 vs DP 30 como las {\'u}nicas estad{\'i}sticamente diferentes. La morfolog{\'i}a de los patrones de grabado {\'a}cido del esmalte evaluados con el microscopio electr{\'o}nico de barrido mostr{\'o} que a mayor tempo de grabado, m{\'a}s profundo era el efecto en el esmalte. Los patrones del grabado obtenidos en esmalte tratado con el papel de SiC fueron m{\'a}s uniformes que los obtenidos en el esmalte tratado solo con piedra p{\'o}mez. El esmalte acondicionado fue perfectamente penetrado con la resina de uni{\'o}n. En la mayor{\'i}a de los casos, los espec{\'i}menes mostraron falla cohesiva de la resina muy proxima a la interface con el esmalte. 1994 BSPD, IAPD and Blackwell Publishing Ltd",
author = "S. MALFERRARI and FINGER, {W. J.} and Franklin Garcia-Godoy",
year = "1994",
month = "1",
day = "1",
doi = "10.1111/j.1365-263X.1994.tb00138.x",
language = "English (US)",
volume = "4",
pages = "217--224",
journal = "International Journal of Paediatric Dentistry",
issn = "0960-7439",
publisher = "Wiley-Blackwell",
number = "4",

}

TY - JOUR

T1 - The effect of etching time with Gluma 2000 conditioning solution on shear bond strength of a composite resin and on micromorphology of the enamel

AU - MALFERRARI, S.

AU - FINGER, W. J.

AU - Garcia-Godoy, Franklin

PY - 1994/1/1

Y1 - 1994/1/1

N2 - Summary. The purpose of this study was to assess the effect of etching time with Gluma 2000 conditioning agent on, first, the shear bond strength of composite resin to tooth enamel and, secondly, the micromorphology of the enamel. In the first part of the study flat enamel surfaces were prepared with 600‐grit silicon carbide paper on 40 primary and 40 permanent teeth. Ten specimens of each group were etched for 15, 30, 60 or 120 seconds before applying bonding resin and restorative composite resin. After 24 hours' storage in water, the shear bond strength of each specimen was tested. Analysis of variance indicated a significant difference between the eight groups. However, the Student‐Newman‐Keuls test indicated that the only differences that were significant were the greater bond strengths of the 15‐second primary tooth specimens compared with the 15‐ and 30‐second permanent tooth specimens. In most cases the debonded specimens showed cohesive failure in resin close to the coupling interface. In the second part of the study the morphology of the enamel etching patterns in 96 other teeth was studied by scanning electron microscopy. The patterns were similar in primary and permanent teeth, and the longer the etching time the more pronounced was the pattern. The patterns produced in ground enamel were more uniform and predictable than those in pumiced enamel. Examination of bonded resin surfaces after dissolution of the teeth showed complete reproduction of the etched enamel surfaces, indicating excellent flow of the resin into the etched enamel. Le propos de cette étude est d'évaluer le résultat de la durée d'application d'acide, par l'agent de conditionnement Gluma 2000, sur premièrement la force de résistance du lien à l'émail dentaire et, deuxièment, la micromorphologie de l'émail. Dans la première partie de l'étude, des surfaces d'émail planes de 40 dents temporaires et 40 dents permanentes ont été préparées avec un carbure siliconé de 600 grains. Dix spécimens de chaque groupe ont été mordancés à l'acide pendant 15, 30, 60 ou 120 secondes avant application de l'agent de liaison et obturation avec une résine composite. Après immersion dans l'eau pendant vingt‐quatre heures, la résistance de la liaison de l'obturation à chaque spécimen a été testée. l'analyse de variance a montré des différences significatives entre les huit groupes. Mais, le test Student‐Newman‐Keuls a montré que les seules différences significatives étaient la résistance plus importante de la liaison aux 15 molaires temporaires mordancées à l'acide 15 secondes, comparée à celles des dents permanentes traitées 15 et 30 secondes. Dans la majorité des cas, les obturations descellées montraient un défaut de cohésion au niveau de l'interface. Dans la seconde partie de l'étude, la morphologie de l'émail, mordancé à l'acide, de 96 autres dents, a été étudiée au microscope électronique à balayage. Les résultats étaient similaires pour les dents temporaires et permanentes et plus marqués, quand le temps d'application était plus long. Les résultats étaient plus uniformes et prévisibles dans l'émail meulé que dans l'émail poli. l'examen des surfaces de liaison à la résine, après dissolution de la dent, montrait une reproduction des surfaces d'émail mordancé à l'acide; la résine avait donc obturé de façon compléte les microrétentions. Ziel der vorliegenden Untersuchung war die Beurteilung der Wirksamkeit der Gluma 2000 Ätzlösung auf Schmelz von Milchzähnen (DI) und von bleibenden Zähnen (DP). Im ersten Teil der Studie wurden von 40 Milchzähnen (DI) und von 40 bleibenden Zähnen (DP) Schmelzoberflächen mit Sic‐Papier der Körnung 600 präpariert. Zehn Proben jeder Gruppe wurden für 15, 30, 60 oder 120 Sekunden vor Applikation des Haftmittels und Restaurirungskunststoffes geätzt. Nach 24 stündiger lagerung in Wasser wurde vonjeder Probe die Scherbindungsfestigkeit bestimmt. Die Varianz‐analyse zeigte signifkante Unterschiede zwischen acht Gruppen (p = 0.003). Nach dem Student‐Newman‐Keuls Test erwiesen sich nur die Vergleiche DI15 vs DI15 und DI15 vs DP30 als signifikant unterschiedlich. Im zweiten Teil der Studie wurde die Morphologie der Schmelzätzmuster an 96 weiteren Zähnen im Rasterelektronermikroskop untersucht. Je länger die Ätzdauer, umso ausgeprägter war das Ätzmuster. Die auf präpariertem Schmelz erzeugten Äztmuster waren gleichmässiger und vorhersehbarer als die auf nur mit Bimsstein‐behandeltem Schmelz. Der geätzte Schmelz wurde vom adhäsiven Resin vollständig benetzt. Nach Auflösung der Zähne kannte man die vollständigewiedergabe der geäzten Schmelzflächen sehen, was auf den ausergewöhnlichen guten Flow des Kunststoffes in den angeäzten Schmelz hinweist. El Propósito de este trabajo fue evaluar la eficacia de la solución acondicionadora de oxalato de aluminio del agente de unión Gluma 2000 en el esmalte de dientes temporales (DI) y permanentes (DP). Para evaluar la fuerza de unión (SBS) 24 horas despues de almacenar los especímenes en agua, en 40 DI y DP se produjo una superficie plana con papel de SiC grado 600. Diez especímenes de cada grupo fueron grabados por 15, 30, 60 y 120 segundos antes de aplicar el agente de unión y la resina restauradora Pekafill. El análisis de varianza mostró que hubo diferencia significativa (P = 0.0003) entre los 8 grupos. La prueba de Student‐Newman‐Keuls identificó las comparaciones DI15 vs DP15 y DI15 vs DP 30 como las únicas estadísticamente diferentes. La morfología de los patrones de grabado ácido del esmalte evaluados con el microscopio electrónico de barrido mostró que a mayor tempo de grabado, más profundo era el efecto en el esmalte. Los patrones del grabado obtenidos en esmalte tratado con el papel de SiC fueron más uniformes que los obtenidos en el esmalte tratado solo con piedra pómez. El esmalte acondicionado fue perfectamente penetrado con la resina de unión. En la mayoría de los casos, los especímenes mostraron falla cohesiva de la resina muy proxima a la interface con el esmalte. 1994 BSPD, IAPD and Blackwell Publishing Ltd

AB - Summary. The purpose of this study was to assess the effect of etching time with Gluma 2000 conditioning agent on, first, the shear bond strength of composite resin to tooth enamel and, secondly, the micromorphology of the enamel. In the first part of the study flat enamel surfaces were prepared with 600‐grit silicon carbide paper on 40 primary and 40 permanent teeth. Ten specimens of each group were etched for 15, 30, 60 or 120 seconds before applying bonding resin and restorative composite resin. After 24 hours' storage in water, the shear bond strength of each specimen was tested. Analysis of variance indicated a significant difference between the eight groups. However, the Student‐Newman‐Keuls test indicated that the only differences that were significant were the greater bond strengths of the 15‐second primary tooth specimens compared with the 15‐ and 30‐second permanent tooth specimens. In most cases the debonded specimens showed cohesive failure in resin close to the coupling interface. In the second part of the study the morphology of the enamel etching patterns in 96 other teeth was studied by scanning electron microscopy. The patterns were similar in primary and permanent teeth, and the longer the etching time the more pronounced was the pattern. The patterns produced in ground enamel were more uniform and predictable than those in pumiced enamel. Examination of bonded resin surfaces after dissolution of the teeth showed complete reproduction of the etched enamel surfaces, indicating excellent flow of the resin into the etched enamel. Le propos de cette étude est d'évaluer le résultat de la durée d'application d'acide, par l'agent de conditionnement Gluma 2000, sur premièrement la force de résistance du lien à l'émail dentaire et, deuxièment, la micromorphologie de l'émail. Dans la première partie de l'étude, des surfaces d'émail planes de 40 dents temporaires et 40 dents permanentes ont été préparées avec un carbure siliconé de 600 grains. Dix spécimens de chaque groupe ont été mordancés à l'acide pendant 15, 30, 60 ou 120 secondes avant application de l'agent de liaison et obturation avec une résine composite. Après immersion dans l'eau pendant vingt‐quatre heures, la résistance de la liaison de l'obturation à chaque spécimen a été testée. l'analyse de variance a montré des différences significatives entre les huit groupes. Mais, le test Student‐Newman‐Keuls a montré que les seules différences significatives étaient la résistance plus importante de la liaison aux 15 molaires temporaires mordancées à l'acide 15 secondes, comparée à celles des dents permanentes traitées 15 et 30 secondes. Dans la majorité des cas, les obturations descellées montraient un défaut de cohésion au niveau de l'interface. Dans la seconde partie de l'étude, la morphologie de l'émail, mordancé à l'acide, de 96 autres dents, a été étudiée au microscope électronique à balayage. Les résultats étaient similaires pour les dents temporaires et permanentes et plus marqués, quand le temps d'application était plus long. Les résultats étaient plus uniformes et prévisibles dans l'émail meulé que dans l'émail poli. l'examen des surfaces de liaison à la résine, après dissolution de la dent, montrait une reproduction des surfaces d'émail mordancé à l'acide; la résine avait donc obturé de façon compléte les microrétentions. Ziel der vorliegenden Untersuchung war die Beurteilung der Wirksamkeit der Gluma 2000 Ätzlösung auf Schmelz von Milchzähnen (DI) und von bleibenden Zähnen (DP). Im ersten Teil der Studie wurden von 40 Milchzähnen (DI) und von 40 bleibenden Zähnen (DP) Schmelzoberflächen mit Sic‐Papier der Körnung 600 präpariert. Zehn Proben jeder Gruppe wurden für 15, 30, 60 oder 120 Sekunden vor Applikation des Haftmittels und Restaurirungskunststoffes geätzt. Nach 24 stündiger lagerung in Wasser wurde vonjeder Probe die Scherbindungsfestigkeit bestimmt. Die Varianz‐analyse zeigte signifkante Unterschiede zwischen acht Gruppen (p = 0.003). Nach dem Student‐Newman‐Keuls Test erwiesen sich nur die Vergleiche DI15 vs DI15 und DI15 vs DP30 als signifikant unterschiedlich. Im zweiten Teil der Studie wurde die Morphologie der Schmelzätzmuster an 96 weiteren Zähnen im Rasterelektronermikroskop untersucht. Je länger die Ätzdauer, umso ausgeprägter war das Ätzmuster. Die auf präpariertem Schmelz erzeugten Äztmuster waren gleichmässiger und vorhersehbarer als die auf nur mit Bimsstein‐behandeltem Schmelz. Der geätzte Schmelz wurde vom adhäsiven Resin vollständig benetzt. Nach Auflösung der Zähne kannte man die vollständigewiedergabe der geäzten Schmelzflächen sehen, was auf den ausergewöhnlichen guten Flow des Kunststoffes in den angeäzten Schmelz hinweist. El Propósito de este trabajo fue evaluar la eficacia de la solución acondicionadora de oxalato de aluminio del agente de unión Gluma 2000 en el esmalte de dientes temporales (DI) y permanentes (DP). Para evaluar la fuerza de unión (SBS) 24 horas despues de almacenar los especímenes en agua, en 40 DI y DP se produjo una superficie plana con papel de SiC grado 600. Diez especímenes de cada grupo fueron grabados por 15, 30, 60 y 120 segundos antes de aplicar el agente de unión y la resina restauradora Pekafill. El análisis de varianza mostró que hubo diferencia significativa (P = 0.0003) entre los 8 grupos. La prueba de Student‐Newman‐Keuls identificó las comparaciones DI15 vs DP15 y DI15 vs DP 30 como las únicas estadísticamente diferentes. La morfología de los patrones de grabado ácido del esmalte evaluados con el microscopio electrónico de barrido mostró que a mayor tempo de grabado, más profundo era el efecto en el esmalte. Los patrones del grabado obtenidos en esmalte tratado con el papel de SiC fueron más uniformes que los obtenidos en el esmalte tratado solo con piedra pómez. El esmalte acondicionado fue perfectamente penetrado con la resina de unión. En la mayoría de los casos, los especímenes mostraron falla cohesiva de la resina muy proxima a la interface con el esmalte. 1994 BSPD, IAPD and Blackwell Publishing Ltd

UR - http://www.scopus.com/inward/record.url?scp=0028725737&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=0028725737&partnerID=8YFLogxK

U2 - 10.1111/j.1365-263X.1994.tb00138.x

DO - 10.1111/j.1365-263X.1994.tb00138.x

M3 - Article

VL - 4

SP - 217

EP - 224

JO - International Journal of Paediatric Dentistry

JF - International Journal of Paediatric Dentistry

SN - 0960-7439

IS - 4

ER -